Boardsort.com

Your complete E-scrap resource website. LEARN - SELL - PROFIT
It is currently Sat Nov 18, 2017 1:59 pm


Post new topic Reply to topic  [ 6 posts ] 
Author Message
 Post subject: few more..27
PostPosted: Sun Sep 25, 2016 9:33 pm 

Joined: Sat Mar 26, 2016 9:54 am
Posts: 371
Location: Mississippi
Attachment:
File comment: Tear down or not to tear down, that is the million dollar question. Curiosity says tear it down, let's see what's inside. But it says laser product ,so I am asking you.
20160925_202800.jpg
20160925_202800.jpg [ 2.06 MiB | Viewed 471 times ]


Top
 Profile  
 
 Post subject: Re: few more..27
PostPosted: Mon Sep 26, 2016 1:28 am 

Joined: Tue Feb 03, 2015 6:57 pm
Posts: 3536
Location: Low DOS
Mobile CD player.
Nothing dangerous. As long as it's not turned on. Lol.
Shell is stainless, controller board, some tiny peripheral boards, motor, stainless rails (308 or 400 series) flat wire. Not much there but worth more apart than together for scrap.

_________________
-- my grades are my own and do not represent an offer from boardsort, nor are they guaranteed. Please keep that in mind.


Top
 Profile  
 
 Post subject: Re: few more..27
PostPosted: Mon Sep 26, 2016 2:32 am 

Joined: Sat Jun 07, 2014 7:29 am
Posts: 38
I didn't realise that the shell was stainless. I have always thought that they were aluminium, especially because they didn't spark?


Top
 Profile  
 
 Post subject: Re: few more..27
PostPosted: Mon Sep 26, 2016 6:45 am 

Joined: Sat Mar 26, 2016 9:54 am
Posts: 371
Location: Mississippi
Lostinlodos, you said controller board, is that different from a cd/dvd board?
And ,flippy, I have found that depending on the grade of SS (stainless steel) that it may not spark, I usually do the scratch test, easy too scratch, aluminum and hard to scratch SS.


Top
 Profile  
 
 Post subject: Re: few more..27
PostPosted: Mon Sep 26, 2016 11:46 am 

Joined: Tue Feb 03, 2015 6:57 pm
Posts: 3536
Location: Low DOS
Stainless with nickel will spark.
With aluminium or magnesium will not. 308 doesn't usually spark.
Actually the best I've found for me is to look under a fluorescent tube, an old shop light. Stainless will always have multiple colours in the stripes, aluminium will look like different shades of silver and grey.

But the best way is to get an old 5 meg hard drive and pull the cobalt magnet from it. No matter how little the iron or nickel et al content is it will still stick or drag.

Great for permanently wiping tapes too ! Just rewind the tape to one end. Place magnet over clear plastic window for a few hours and you've got a blank tape. Be it pcdat or vhs or anything else. Though the tape will never work again.

_________________
-- my grades are my own and do not represent an offer from boardsort, nor are they guaranteed. Please keep that in mind.


Top
 Profile  
 
 Post subject: Re: few more..27
PostPosted: Mon Sep 26, 2016 11:47 am 

Joined: Tue Feb 03, 2015 6:57 pm
Posts: 3536
Location: Low DOS
Lisa, it will be at least a cd/DVD board but could also go as telco depending on factors.

_________________
-- my grades are my own and do not represent an offer from boardsort, nor are they guaranteed. Please keep that in mind.


Top
 Profile  
 
Display posts from previous:  Sort by  
Post new topic Reply to topic  [ 6 posts ] 

All times are UTC - 5 hours [ DST ]


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Jump to:  

cron