It’s usually stamped as such. Beyond that it’s practice.

_________________
-- my grades are my own and do not represent an offer from boardsort, nor are they guaranteed. Please keep that in mind.


Top
 Profile  
 
PostPosted: Sun Jul 08, 2018 7:17 am 

Joined: Tue Jun 19, 2018 4:52 pm
Posts: 129
flyfish2k wrote:
how do you test for Magnesium?

Don't try the old "flame test" for magnesium. If you heat it with the propane torch, it will ignite and burn with a brilliant blue-white flame until nothing is left but a powdery ash. I learned this when trying to cut out rusty bolts from junk lawnmower frames years ago


Top
 Profile  
 
PostPosted: Sun Jul 08, 2018 4:11 pm 
Site Admin
User avatar

Joined: Tue Feb 03, 2015 6:57 pm
Posts: 7471
Location: Low DOS
David: absolutely correct. Magnesium is a very volatile metal.
Magnesium flame testing... you’re not actually burning it but igniting it.
Magnesium is used in Roman candles, aerial fireworks, and MOST fire based fuses. Gives off beautiful sparks.

So how do you tell magnesium from manganese? Well I guess the fastest way is to make a pile and set it on fire.
Anything left over that is metal is manganese. The powder is un-scrapable magnesium oxide.
Makes great fertiliser for conifers though! ;)

Bottom line is don’t. Just a bad idea. And if you must, NEVER throw water on the blase. You get instantaneous oxidation and hydrogen release creating a big explosion, 10,000•+ flame, a blinding (as in never see again) flash, and that’s assuming you survive the heat blast.

_________________
-- my grades are my own and do not represent an offer from boardsort, nor are they guaranteed. Please keep that in mind.


Top
 Profile  
 
PostPosted: Thu Jul 26, 2018 12:40 pm 

Joined: Tue Jun 03, 2014 2:15 pm
Posts: 104
You can place those top covers of steel and stainless steel in an old pot (not one your wife cooks with) and heat the water to boil and the glue holding the two metals will get loose and you can put shred in one pile and stainless in another


Top
 Profile  
 
PostPosted: Fri Jul 24, 2020 10:47 am 

Joined: Fri Jun 12, 2020 3:40 pm
Posts: 13
Lost,
I too have a good amount of hard drive actuators that i pulled the tips, wire, and little control boards. My question is must you pull the little square head off the metal or can you simply snip the end of the reader head with metal attached?
And you mentioned the boards, are you referring to the small boards mounted to the side of the actuator arm?

I attached a photo to show you what i mean, is the one on the far right acceptable or must it be removed from the metal? Thanks Lost!


Attachments:
HDReaderTips.jpg
HDReaderTips.jpg [ 516.91 KiB | Viewed 631 times ]
Top
 Profile  
 
PostPosted: Fri Jul 24, 2020 1:16 pm 
Site Admin
User avatar

Joined: Tue Feb 03, 2015 6:57 pm
Posts: 7471
Location: Low DOS
mjm316 wrote:
..!

If you are sniping for rhodium there not much of a loss in just snipping the metal end while. I found my current buyer only “fees” on it about 6%. Just minimise the extra metal to stay in recovery vs breakage.

_________________
-- my grades are my own and do not represent an offer from boardsort, nor are they guaranteed. Please keep that in mind.


Top
 Profile  
 
Display posts from previous:  Sort by  
Post new topic Reply to topic  [ 36 posts ]  Go to page Previous  1, 2, 3, 4

All times are UTC - 5 hours [ DST ]


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Jump to: